5013f04 TOPAS薄膜原料
- 品牌：5013f04
- 货号：RXT85A
- 价格： ￥62/千克
- 发布日期： 2023-04-25
- 更新日期： 2024-04-29
产品详请
| 品牌 | 5013f04 |
| 货号 | RXT85A |
| 牌号 | 5013L-10 |
| 型号 | 5013f04 |
| 品名 | COC |
| 外形尺寸 | RxT90A |
| 产品用途 | 配件 |
| 生产企业 | RxT90A |
| 是否进口 | 否 |
5013f04 TOPAS薄膜原料
Product Description
TOPAS 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorphous resin with high flow, high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer cast blends, and in coextruded blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS.
Selected Applications
Leading Attributes
Related Grades for Packaging and Film Extrusion
TOPAS 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorphous resin with high flow, high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer cast blends, and in coextruded blends in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear packaging. If performance at elevated temperatures is not required, we also offer lower glass transition temperature (Tg) grades of TOPAS.
Selected Applications
- Decorative film and sheet
- General packaging
- Food packaging
- Blown film
- Healthcare and food contact
Leading Attributes
- Gloss, hardness, chemical resistance, forming
- Easy or linear tear, heat resistance, hot fill, gloss
- Not manufactured with BPA, phthalates, or halogens
- High strength and high productivity
- Broad regulatory compliance
Related Grades for Packaging and Film Extrusion
- TOPAS 6013F-04 - high temperature grade with standard flow
物性信息：
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| 形式 |
|
| 加工方法 |
|
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 1.02 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） | ISO 1133 | ||
| 190°C/2.16 kg | < 0.10 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 8.0 | g/10 min | ISO 1133 |
| 溶化体积流率（MVR） | ISO 1133 | ||
| 190°C/2.16 kg | < 0.100 | cm3/10min | ISO 1133 |
| 230°C/2.16 kg | 9.00 | cm3/10min | ISO 1133 |
| 吸水率 (饱和, 23°C) | 0.010 | % | ISO 62 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 70 | μm | |
| 拉伸模量 | ISO 527-3/1 | ||
| MD : 70 μm, 铸造薄膜 | 2600 | MPa | ISO 527-3/1 |
| TD : 70 μm, 铸造薄膜 | 2500 | MPa | ISO 527-3/1 |
| 拉伸应力 | ISO 527-3/50 | ||
| MD : 断裂, 70 μm, 铸造薄膜 | 35.0 | MPa | ISO 527-3/50 |
| TD : 断裂, 70 μm, 铸造薄膜 | 25.0 | MPa | ISO 527-3/50 |
| 伸长率 | ISO 527-3/50 | ||
| MD : 断裂, 70 μm, 铸造薄膜 | 1.4 | % | ISO 527-3/50 |
| TD : 断裂, 70 μm, 铸造薄膜 | 1.1 | % | ISO 527-3/50 |
| 落锤冲击 (70 μm, 铸造薄膜) | < 36 | g | ISO 7765-1 |
| 埃尔曼多夫抗撕强度 | ISO 6383-2 | ||
| MD : 70 μm, 铸造薄膜 | 0.11 | N | ISO 6383-2 |
| TD : 70 μm, 铸造薄膜 | 0.11 | N | ISO 6383-2 |
| 透氧率 (23°C, 70 μm, 挤塑薄膜, 50% RH) | 26 | cm3·mm/m2/atm/24 hr | ASTM D3985 |
| 水气透过率 (70 μm, 38°C, Cast Film, 90% RH) | 0.14 | g·mm/m2/atm/24 hr | ASTM F1249 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 玻璃转化温度 | 134 | °C | ISO 11357-2 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 光泽度 (60°, 70.0 μm, 铸造薄膜) | > 100 | ISO 2813 | |
| 雾度 (70.0 μm, 铸造薄膜) | < 1.0 | % | ISO 14782 |
| 挤出 | 额定值 | 单位制 | |
|---|---|---|---|
| 挤塑机进料部分 | 20 到 70 | °C | |
| 挤出机螺杆长径比L / D | > 28:1 | ||
| 料筒1区温度 | 220 到 240 | °C | |
| 料筒2区温度 | 220 到 240 | °C | |
| 料筒3区温度 | 220 到 240 | °C | |
| 料筒4区温度 | 220 到 240 | °C | |
| 口模温度 | 220 到 240 | °C |