60微米 EOS PA 2200 Top Speed 1.0
EOS PA 2200 Top Speed 1.0
Typical applications of the material are fully functional plastic parts of highest quality. Due to the excellent mechanical properties the material is often used to substitute typical injection moulding plastics. The biocompatibility allows its use e.g. for prostheses, the high abrasion resistance allows e.g. the realisation of movable part connections.
180 μm layer thickness:
TopSpeed is a very economical parameter set for parts with medium to high requirements of quality and mechanical load and high cost pressure. Particularly large and relatively thick-walled parts can usually profit from this layer thickness, mostly without any noticeable impairment from the fast build-up rates.
基本信息
特性
用途
机构评级
外观
形式
加工方法
物理性能
额定值
单位制
测试方法
密度
0.930
g/cm3
内部方法
Thickness - Layer
180.0
μm
硬度
额定值
单位制
测试方法
肖氏硬度 (邵氏 D, 15 秒)
75
ISO 868
机械性能
额定值
单位制
测试方法
拉伸模量 1
1500
MPa
ISO 527-2
拉伸应力
-- 2
38.0
MPa
ISO 527-2
-- 3
45.0
MPa
ISO 527-2
拉伸应变
断裂 4
18
%
ISO 527-2
断裂 5
3.0
%
ISO 527-2
弯曲模量 6(23°C)
1500
MPa
ISO 178
冲击性能
额定值
单位制
测试方法
简支梁缺口冲击强度 7(23°C)
4.8
kJ/m2
ISO 179/1eA
简支梁无缺口冲击强度 8(23°C)
53
kJ/m2
ISO 179/1eU
悬壁梁缺口冲击强度 (23°C)
4.4
kJ/m2
ISO 180/1A
热性能
额定值
单位制
测试方法
维卡软化温度
163
°C
ISO 306/B50
熔融温度
176
°C
ISO 11357