本色超高韧性 Fortron 1140L4 SF3001
  • 品牌:1140L4 SF3001
  • 货号:200
  • 价格: ¥43/千克
  • 发布日期: 2023-02-16
  • 更新日期: 2024-03-01
产品详请
品牌 1140L4 SF3001
货号 200
牌号 1140L4 SF3001
型号 1140L4 SF3001
品名 PPS
外形尺寸 100
产品用途 配件
生产企业 SF3001
是否进口

本色超高韧性 Fortron 1140L4 SF3001


Fortron 1140L4 is a 40% glass-reinforced grade that is the strongest and toughest product available. It exhibits excellent heat and chemical resistance, good electrical properties and is inherently flame-retardant. The high hardness and rigidity at elevated temperatures allows for good load bearing performance. This product has good weldability due to the modest filler level. Applications made of this grade are electronical components (i.e. bobbins, lamp housings, brush holders) and various other components requiring strength and resistance to aggressive chemicals (i.e. automotive heaters, pumps, valves, fuel rails, microwave oven rings and distillation column packings).

物性信息:
基本信息
黄卡编号
  • E107854-237735
  • E107854-237738
  • E107854-237739
填料/增强材料
  • 玻璃纤维增强材料, 40% 填料按重量
特性
  • 超高韧性
  • 刚性,高
  • 高强度
  • 可焊接
  • 良好的电气性能
  • 耐化学性良好
  • 耐热性,高
  • 硬度高
  • 阻燃性
用途
  • 泵件
  • 电气/电子应用领域
  • 阀门/阀门部件
  • 汽车领域的应用
  • 外壳
RoHS 合规性
  • 联系制造商
多点数据
  • Isochronous Stress vs. Strain (ISO 11403-1)
  • Isothermal Stress vs. Strain (ISO 11403-1)
  • Shear Modulus vs. Temperature (ISO 11403-1)

物理性能 额定值 单位制 测试方法
比重 1.65 g/cm3 ASTM D792, ISO 1183
特定体积 0.611 cm3/g ASTM D792
充模分析 额定值 单位制 测试方法
Specific Heat Capacity of Melt 1500 J/kg/°C 内部方法
补充信息 额定值 单位制 测试方法
Specimen Thickness - Shrinkage 3.18 mm 内部方法
物理性能 额定值 单位制 测试方法
收缩率
    流动 0.20 到 0.30 % ASTM D955
    横向流动 0.50 到 0.70 % ASTM D955
    垂直流动方向 0.40 到 0.60 % ISO 294-4
    流动方向 0.20 到 0.60 % ISO 294-4
吸水率 (饱和, 23°C) 0.020 % ISO 62
硬度 额定值 单位制 测试方法
洛氏硬度
    M 级 100 ASTM D785
    M 计秤 100 ISO 2039-2
机械性能 额定值 单位制 测试方法
拉伸模量
    -40°C 14500 MPa ASTM D638
    75°C 11900 MPa ASTM D638
    150°C 4270 MPa ASTM D638
    200°C 3240 MPa ASTM D638
    -- 14700 MPa ISO 527-2/1A/1
抗张强度
    断裂, 23°C 200 MPa ASTM D638
    断裂 195 MPa ISO 527-2/1A/5
伸长率
    断裂, 23°C 1.7 % ASTM D638
    断裂 1.9 % ISO 527-2/1A/5
弯曲模量 (23°C) 14500 MPa ISO 178
弯曲应力 1 285 MPa ISO 178
冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度 ISO 179/1eA
    -30°C 10 kJ/m2 ISO 179/1eA
    23°C 10 kJ/m2 ISO 179/1eA
简支梁无缺口冲击强度 ISO 179/1eU
    -30°C 53 kJ/m2 ISO 179/1eU
    23°C 53 kJ/m2 ISO 179/1eU
悬壁梁缺口冲击强度 ISO 180/1A
    -30°C 10 kJ/m2 ISO 180/1A
    23°C 10 kJ/m2 ISO 180/1A
无缺口伊佐德冲击强度 (23°C) 34 kJ/m2 ISO 180/1U
热性能 额定值 单位制 测试方法
载荷下热变形温度
    0.45 MPa, 退火 280 °C ASTM D648
    1.8 MPa, 未退火 265 °C ASTM D648
    1.8 MPa, 未退火 270 °C ISO 75-2/A
    8.0 MPa, 未退火 215 °C ISO 75-2/C
玻璃转化温度 2 90.0 °C ISO 11357-2
熔融温度 3 280 °C ISO 11357-3
线形热膨胀系数 ISO 11359-2
    流动 2.6E-5 cm/cm/°C ISO 11359-2
    横向 4.2E-5 cm/cm/°C ISO 11359-2
电气性能 额定值 单位制 测试方法
表面电阻率 > 1.0E+15 ohms IEC 60093
体积电阻率
    -- 1.0E+16 ohms·cm ASTM D257
    -- > 1.0E+15 ohms·cm IEC 60093
介电强度 28 kV/mm IEC 60243-1
介电常数
    1 kHz 3.50 ASTM D150
    1 MHz 3.50 ASTM D150
    1 MHz 4.60 IEC 60250
耗散因数
    1 kHz 1.0E-3 ASTM D150
    1 MHz 1.0E-3 ASTM D150
    1 MHz 6.2E-3 IEC 60250
耐电弧性 134 sec ASTM D495
漏电起痕指数 125 V IEC 60112
可燃性 额定值 单位制 测试方法
UL 阻燃等级 UL 94
    0.380 mm V-0 UL 94
    1.50 mm V-0 UL 94
    3.00 mm 5VA UL 94
极限氧指数 47 % ISO 4589-2

注射 额定值 单位制
干燥温度 130 到 140 °C
干燥时间 3.0 到 4.0 hr
建议的 水分含量 0.020 %
料斗温度 20.0 到 30.0 °C
料筒后部温度 290 到 300 °C
料筒中部温度 310 到 320 °C
料筒前部温度 330 到 340 °C
射嘴温度 310 到 330 °C
加工(熔体)温度 330 到 340 °C
模具温度 140 到 160 °C
注塑压力 50.0 到 100 MPa
注射速度 快速
保压 30.0 到 70.0 MPa
背压 0.00 到 3.00 MPa

是一种摩擦学改性Fortron®-含40%玻璃纤维的聚苯硫醚。Fortron 6341L4具有与Fortron 1342L4相同的机械性能,但具有不同的摩擦学调整。








(PPS)是一种部分结晶的高温性能聚合物,是综合性能优异的特种工程塑料。PPS具有优良的耐高温、耐腐蚀、耐辐射、阻燃、均衡的物理机械性能和极好的尺寸稳定性以及优良的电性能等特点,被广泛用作结构性高分子材料,通过填充、改性后广泛用作特种工程塑料。同时,PPS还可制成各种功能性的薄膜、涂层和复合材料,在电子电器、航天、汽车运输等领域获得成功应用。近年来,国内企业积极研发,并初步形成了一定的生产能力,改变了以往完全依赖进口的状况。但国内PPS技术还存在产品品种少、高功能产品少、产能急待扩大等问题,这些将是PPS下一步发展的重点。PPS产品拥有不同的形式和等级,例如树脂、纤维、长丝、薄膜以及涂层等,应用十分广泛,已成为汽车工业、电子电器、机械化工、 国防、纺织工业、环保行业等领域不可或缺的材料之一。特别是近几年,各国对于新能源汽车产业的推动,进一步带动了PPS市场快速发展。据化工咨询公司Prismane Consulting战略咨询报告显示,新能源汽车行业已成为PPS下游驱动力,应用占比达到41%,其次是电子电器领域占比20%。PPS应用广泛,故与各种替代产品相互竞争,这些替代品包括金属(如不锈钢、铜、铝、合金等)、各种工程塑料等。在汽车和电器产品中,PPS与PPA、LCP、PAI、PEK、PEEK、PEI可相互替代使用,性价比是影响下游客户采购的核心因素。