自然色Pibiflex 5612 5880 Taro Plast
Availability
|
|
|||
Processing Method
|
|
Physical |
Nominal Value
|
Unit
|
Test Method
|
Density
|
1.24
|
g/cm3
|
ISO 1183 |
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)
|
15
|
g/10 min
|
ISO 1133 |
Hardness |
Nominal Value
|
Unit
|
Test Method
|
Shore Hardness (Shore D, 15 sec)
|
54
|
|
ISO 868 |
Mechanical |
Nominal Value
|
Unit
|
Test Method
|
Flexural Modulus (23°C)
|
300
|
MPa
|
ISO 178 |
Elastomers |
Nominal Value
|
Unit
|
Test Method
|
Tensile Stress (Break)
|
38.0
|
MPa
|
ISO 37 |
Tensile Elongation (Break)
|
500
|
%
|
ISO 37 |
Impact |
Nominal Value
|
Unit
|
Test Method
|
Charpy Notched Impact Strength (23°C)
|
No Break
|
|
ISO 179/1eA |
Notched Izod Impact Strength (23°C)
|
No Break
|
|
ISO 180/1A |
Thermal |
Nominal Value
|
Unit
|
Test Method
|
Vicat Softening Temperature
|
196
|
°C
|
ISO 306/A50 |
Melting Temperature 1
|
218
|
°C
|
ISO 11357-3 |
Flammability |
Nominal Value
|
Unit
|
Test Method
|
Oxygen Index
|
20
|
%
|
ISO 4589-2 |
Injection |
Nominal Value
|
Unit
|
|
Drying Temperature
|
100 to 110
|
°C
|
|
Drying Time
|
4.0
|
hr
|
|
Suggested Max Moisture
|
0.050
|
%
|
|
Injection Feed Temperature
|
20 to 50
|
°C
|
|
Rear Temperature
|
210 to 220
|
°C
|
|
Middle Temperature
|
230 to 250
|
°C
|
|
Front Temperature
|
235 to 255
|
°C
|
|
Injection Zone 4 Temperature
|
235 to 255
|
°C
|
|
Nozzle Temperature
|
245 to 265
|
°C
|
|
Processing (Melt) Temp
|
240 to 260
|
°C
|
|
Mold Temperature
|
45 to 55
|
°C
|
|
Hot Runner
|
235 to 255
|
°C
|