| 品牌 | ALE-85A |
| 货号 | 100 |
| 用途 | 配件 |
| 牌号 | ALE-85A-B30 |
| 型号 | ALE-85A |
| 品名 | ALE-85A-B30 Biomerics Quadraflex经销商 |
| 包装规格 | 25kg |
| 外形尺寸 | 25kg |
| 生产企业 | Biomerics |
| 是否进口 | 是 |
ALE-8*-B30 Biomerics Quadraflex经销商
Product Description:
Quadraflex™ ALE-8*-B20 is high performance aliphatic polyether thermoplastic polyurethane. The polymer is loaded with 20% barium sulfate by weight, is naturally white and supplied in small pellets for ease of processing. The material exhibits excellent mechanical properties, oxidative stability, biocompatibility, elasticity, non--yellowing during aging and softening at body temperature. The resin has consistent melt flow properties making it ideal for extrusion.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 / 比重 | 1.24 | g/cm3 | ASTM D792 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238 |
| 收缩率 - 流动 | 0.60 到 1.0 | % | ASTM D955 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 肖氏硬度 (邵氏 A) | 85 | | ASTM D2240 |
| | | ||
| 弹性体 | 额定值 | 单位制 | 测试方法 |
| Tensile Stress (10% Strain) | 4.83 | MPa | ASTM D412 |
| 拉伸应力 | | | ASTM D412 |
| 应变 | 7.58 | MPa | |
| 300%应变 | 15.2 | MPa | |
| 抗张强度 (断裂) | 35.9 | MPa | ASTM D412 |
| 伸长率 (断裂) | 500 | % | ASTM D412 |
| 热固性 | 额定值 | 单位制 | |
| 后固化时间 (38°C) | 6.0 到 10 | hr | |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 54 | °C | |
| 干燥时间 | 4.0 | hr | |
| 建议的*水分含量 | < 3.0E-3 | % | |
| 料筒后部温度 | 177 | °C | |
| 料筒前部温度 | 191 | °C | |
| 射嘴温度 | 196 | °C | |
| 加工（熔体）温度 | 204 | °C | |
| 模具温度 | 4 到 32 | °C | |
| 注射速度 | 慢 | | |
| 螺杆压缩比 | 2.5:1.0 到 3.5:1.0 | | |
| 注射说明 | |||
| Injection Speed: 10 g/sec | |||
| 挤出 | 额定值 | 单位制 | |
| 干燥温度 | 54 | °C | |
| 干燥时间 | 4.0 | hr | |
| 建议的*水分含量 | < 0.030 | % | |
| 料筒1区温度 | 171 | °C | |
| 料筒2区温度 | 182 | °C | |
| 料筒3区温度 | 188 | °C | |
| 料筒4区温度 | 193 | °C | |
| 熔体温度 | 193 | °C | |
| 口模温度 | 193 到 216 | °C | |
| 背压 | 6.89 到 12.4 | MPa | |