| 品牌 | ALE-95A-B20 |
| 货号 | 200 |
| 用途 | 配件 |
| 牌号 | ALE-95A-B20 |
| 型号 | ALE-95A-B20 |
| 品名 | TPU |
| 包装规格 | 25kg |
| 外形尺寸 | 100 |
| 生产企业 | ALE-95A-B20 |
| 是否进口 | 否 |
技术参数 Technical Data
物理性能
PHYSICAL
密度
Density
额定值
Nominal Value
1.26
单位
Units
g/cm3
测试方法
Test Method
ASTM D792
熔体质量流动速率
Melt Flow Rate
190°C，2.16kgu
190℃℃，2.16kg
6.0
9/10min
ASTM D1238
收缩率
Shrinkage
MD
MD
弹性体
Elastomer
拉伸强度
tensile strength
断裂
fracture
10% 应变
10% strain
100% 应变
100% strain
300% 应变
300% strain
0.騅淇60 到 1.0
额定值
Nominal Value
41.4
10.3
%
单位
Units
MPa
MPa
MPa
MPa
ASTM D955
测试方法
Test Method
ASTM D412
ASTM D412
ASTM D412
ASTM D412
ASTM D412
Biomerics ALE-95A-B20 Quadraflex
| | Quadraflex™ ALE-90A-B30 | Biomerics, LLC | TPU-聚醚 |
| | Quadraflex™ ALE-93A | Biomerics, LLC | TPU-聚醚 |
| | Quadraflex™ ALE-93A-B20 | Biomerics, LLC | TPU-聚醚 |
| | Quadraflex™ ALE-93A-B30 | Biomerics, LLC | TPU-聚醚 |
| | Quadraflex™ ALE-95A | Biomerics, LLC | TPU-聚醚 |
| | Quadraflex™ ALE-95A-B20 | Biomerics, LLC | TPU-聚醚 |
TPU(Thermoplastic polyurethanes)名称为热塑性 聚氨酯 弹性体橡胶。主要分为有聚酯 型和聚醚 型之分，它硬度范围宽（60HA-85HD）、耐磨 、耐油，透明，弹性好 ，在日用品 、体育用品、玩具、装饰材料等领域得到广泛应用，无卤阻燃TPU还可以代替软质PVC 以满足越来越多领域的环保要求。
所谓弹性体是指玻璃化温度低于室温度,断裂伸长率>50%，外力撤除后复原性比较好的高分子材料。聚氨酯弹性体是弹性体中比较特殊的一大类，聚氨酯弹性体的硬度范围很宽，性能范围很宽，所以聚氨酯弹性体是介于橡胶和塑料的一类高分子 材料。
可加热塑化，化学结构上没有或很少交联，其分子基本是线性的，然而却存在一定的物理交联。这类聚氨酯 称为TPU
TPU的主要特性有：
硬度范围广：通过改变TPU各反应组分的配比，可以得到不同硬度的产品，而且随着硬度的增加，其产品仍保持良好的弹性和耐磨性 。
机械强度高：TPU制品的承载能力、抗冲击性及减震性能突出。
加工性能好：TPU可采用常见的热塑性材料的加工方法进行加工，如注塑 、挤出 、压延 等等。同时，TPU与某些高分子材料共同加工能够得到性能互补的聚合物合金。
耐油、耐水、耐霉菌。