| | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 比重 | | ASTMD792 | 1.53 | g/cm3 |
| 熔流率（熔体流动速率）(250°C/2.16kg) | | ASTMD1238 | 13 | g/10min |
| 收缩率-流动 | | ASTMD955 | 0.40to1.0 | % |
| 吸水率(23°C,24hr) | | ASTMD570 | 0.080 | % |
| 机械性能 | TensileStrength2(Break,3.20mm) | | ASTMD638 | 123 | MPa |
| 伸长率2(断裂,3.20mm) | | ASTMD638 | 3.0 | % |
| 弯曲模量3(3.20mm) | | ASTMD790 | 7850 | MPa |
| 弯曲强度4(屈服,3.20mm) | | ASTMD790 | 196 | MPa |
| 冲击性能 | 悬壁梁缺口冲击强度(23°C,6.40mm) | | ASTMD256 | 78 | J/m |
| 热性能 | 载荷下热变形温度(0.45MPa,未退火,6.40mm) | | ASTMD648 | 215 | °C |
| 载荷下热变形温度(1.8MPa,未退火,6.40mm) | | ASTMD648 | 210 | °C |
| 熔融峰值温度 | | ASTMD3418 | 223 | °C |
| RTIElec | | UL746 | 140 | °C |
| RTIImp | | UL746 | 130 | °C |
| RTIStr | | UL746 | 140 | °C |
| 电气性能 | 体积电阻率 | | ASTMD257 | 1.0E+16 | ohms·cm |
| 介电强度(1.00mm) | | ASTMD149 | 28 | kV/mm |
| 耐电弧性 | | ASTMD495 | PLC5 | |
| 相比耐漏电起痕指数(CTI)4 | | UL746 | PLC0 | |
| 漏电起痕指数(解决方案A) | | IEC60112 | 600 | V |
| | | | |
| |