碳化软饮料瓶PPA Grivory GV-4H black

产品详请

产品说明：

Semi-aromatic polyamide (PPA) based compound. Glass fibers. Very good thermal properties. Good chemical resistance. Low moisture absorption.

Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North America

Information provided by Lati Industria Termoplastici S.p.A.

物性信息：

物理性能	额定值 (公制)	额定值 (英制)
密度	1.55 g/cc	0.0560 lb/in3
线性成型收缩率,Flow	0.0025 - 0.0050 cm/cm	0.0025 - 0.0050 in/in
线性成型收缩率，横向	0.0060 - 0.0090 cm/cm	0.0060 - 0.0090 in/in

机械性能	额定值 (公制)	额定值 (英制)
抗张强度(断裂)	95.0 MPa @Temperature 150 °C	13800 psi @Temperature 302 °F
	150 MPa @Temperature 120 °C	21800 psi @Temperature 248 °F
	170 MPa @Temperature 90.0 °C	24700 psi @Temperature 194 °F
	195 MPa @Temperature 60.0 °C	28300 psi @Temperature 140 °F
	245 MPa @Temperature 23.0 °C	35500 psi @Temperature 73.4 °F
伸长率 (断裂)	2.2 % @Temperature 23.0 °C	2.2 % @Temperature 73.4 °F
	2.4 % @Temperature 60.0 °C	2.4 % @Temperature 140 °F
	2.5 % @Temperature 90.0 °C	2.5 % @Temperature 194 °F
	4.0 % @Temperature 120 °C	4.0 % @Temperature 248 °F
	6.8 % @Temperature 150 °C	6.8 % @Temperature 302 °F
拉伸模量	5.80 GPa @Temperature 150 °C	841 ksi @Temperature 302 °F
	10.5 GPa @Temperature 120 °C	1520 ksi @Temperature 248 °F
	12.0 GPa @Temperature 90.0 °C	1740 ksi @Temperature 194 °F
	14.0 GPa @Temperature 60.0 °C	2030 ksi @Temperature 140 °F
	17.5 GPa @Temperature 23.0 °C	2540 ksi @Temperature 73.4 °F
简支梁无缺口冲击强度	8.50 J/cm2	40.4 ft-lb/in2
简支梁缺口冲击强度	1.00 J/cm2	4.76 ft-lb/in2

热性能	额定值 (公制)	额定值 (英制)
工作温度, Air	150 °C	302 °F
载荷下热变形温度(0.46 MPa)	290 °C	554 °F
载荷下热变形温度(1.8 MPa)	280 °C	536 °F
维卡软化温度	275 °C @Load 5.00 kg	527 °F @Load 11.0 lb

加工性能	额定值 (公制)	额定值 (英制)
加工（熔体）温度	310 - 340 °C	590 - 644 °F
模具温度	150 - 170 °C	302 - 338 °F
干燥温度	120 - 130 °C @Time 10800 sec	248 - 266 °F @Time 3.00 hour

材料描述		测试方法
ISO Shrinkage - Pressure	60 MPa