Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min

63

MPa

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min

50

MPa

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min

4.5

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min

80

%

ASTM D 638

Tensile Modulus, 50 mm/min / 拉伸模量,50 mm/min

2900

MPa

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距

93

MPa

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距

2550

MPa

ASTM D 790

Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C

587

J/m

ASTM D 256

Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C

54

J

ASTM D 3763

Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50

105

°C

ASTM D 1525

HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火

89

°C

ASTM D 648

HDT, 0.45 MPa, 6.4 mm, unannealed / 热变形温度，0.45 MPa, 6.4 mm, 未退火

103

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed / 热变形温度，1.82 MPa, 6.4 mm, 未退火

94

°C

ASTM D 648

CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动

7.2E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向

7.2E-05

1/°C

ASTM E 831

Relative Temp Index, Elec / 相对热指数， 电性能

85

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

85

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

85

°C

UL 746B

Specific Gravity/比重

1.19

–

ASTM D 792

Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm

0.4 – 0.6

%

SABIC Method

Melt Flow Rate / 熔流率, 260°C/2.16 kgf

10

g/10 min

ASTM D 1238

Arc Resistance, Tungsten {PLC} / 耐电弧性{PLC}

6

PLC Code

ASTM D 495

Hot Wire Ignition {PLC) / 热丝引燃 {PLC)

1

PLC Code

UL 746A

High Voltage Arc Track Rate {PLC} / 高电压电弧起痕速率

2

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC} / 高电流电弧引燃，表面{PLC}

0

PLC Code

UL 746A

Comparative Tracking Index (UL) {PLC} / 漏电起痕指数 (UL) {PLC}

1

PLC Code

UL 746A

UL Recognized, 94V-0 Flame Class Rating (3) / UL认可,94V-0 阻燃等级(3)

1.5

mm

UL 94

UL Recognized, 94-5VA Rating (3) / UL认可,94-5VA 阻燃等级(3)

3

mm

UL 94

UL Recognized, 94-5VB Rating (3) / UL认可,94-5VB 阻燃等级(3)

2.5

mm

UL 94

Drying Temperature / 干燥温度

80 – 90

°C

Drying Time / 干燥时间

3 – 4

hrs

Drying Time (Cumulative) / 干燥时间（累积的）

8

hrs

Maximum Moisture Content / *含湿量

0.04

%

Melt Temperature / 熔体温度

245 – 275

°C

Nozzle Temperature / 注嘴温度

245 – 275

°C

Front – Zone 3 Temperature / 前区3温度

245 – 275

°C

Middle – Zone 2 Temperature / 中区2温度

220 – 265

°C

Rear – Zone 1 Temperature / 后区1温度

220 – 255

°C

Mold Temperature / 模具温度

60 – 80

°C

Back Pressure / 背压

0.3 – 0.7

MPa

Screw Speed / 螺杆速度

40 – 70

rpm

Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比

30 – 80

%

Vent Depth / 排气孔深度

0.038 – 0.076

mm