Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min

57

MPa

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min

5

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min

80

%

ASTM D 638

Tensile Modulus, 50 mm/min / 拉伸模量,50 mm/min

2480

MPa

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距

91

MPa

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距

2480

MPa

ASTM D 790

Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C

534

J/m

ASTM D 256

Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C

106

J/m

ASTM D 256

Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C

54

J

ASTM D 3763

Instrumented IMPACT Total Energy, -30°C / 装有测量仪表的落镖冲击Total Energy，-30°C

40

J

ASTM D 3763

HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火

115

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火

98

°C

ASTM D 648

CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动

7.2E-05

1/°C

ASTM E 831

Thermal Conductivity / 导热系数

0.2

W/m-°C

ASTM C 177

Relative Temp Index, Elec / 相对热指数， 电性能

60

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

60

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

60

°C

UL 746B

Specific Gravity/比重

1.12

–

ASTM D 792

Water Absorption, 24 hours / 吸水率， 24小时

0.1

%

ASTM D 570

Water Absorption, equilibrium, 23C / 吸水率，平衡，23C

0.4

%

ASTM D 570

Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm

0.5 – 0.7

%

SABIC Method

Mold Shrinkage, xflow, 3.2 mm / 模塑收缩量，横向，3.2 mm

0.5 – 0.7

%

SABIC Method

Melt Flow Rate / 熔流率, 230°C/3.8 kgf

7

g/10 min

ASTM D 1238

Arc Resistance, Tungsten {PLC} / 耐电弧性{PLC}

5

PLC Code

ASTM D 495

Hot Wire Ignition {PLC) / 热丝引燃 {PLC)

3

PLC Code

UL 746A

High Voltage Arc Track Rate {PLC} / 高电压电弧起痕速率

2

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC} / 高电流电弧引燃，表面{PLC}

0

PLC Code

UL 746A

Comparative Tracking Index (UL) {PLC} / 漏电起痕指数 (UL) {PLC}

1

PLC Code

UL 746A

UL Recognized, 94HB Flame Class Rating (3) / UL认可，94HB 阻燃等级(3)

1.49

mm

UL 94

CSA (See File for complete listing)

LS88480

File No.

CSA LISTED

Drying Temperature / 干燥温度

80 – 90

°C

Drying Time / 干燥时间

3 – 4

hrs

Drying Time (Cumulative) / 干燥时间（累积的）

8

hrs

Maximum Moisture Content / *含湿量

0.04

%

Melt Temperature / 熔体温度

245 – 275

°C

Nozzle Temperature / 注嘴温度

245 – 275

°C

Front – Zone 3 Temperature / 前区3温度

245 – 275

°C

Middle – Zone 2 Temperature / 中区2温度

220 – 265

°C

Rear – Zone 1 Temperature / 后区1温度

220 – 255

°C

Mold Temperature / 模具温度

60 – 80

°C

Back Pressure / 背压

0.3 – 0.7

MPa

Screw Speed / 螺杆速度

40 – 70

rpm

Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比

30 – 80

%

Vent Depth / 排气孔深度

0.038 – 0.076

mm