| 品牌 | 美国沙伯基础 |
| 货号 | 200 |
| 用途 | 配件 |
| 牌号 | C1204HF |
| 型号 | C1204HF |
| 品名 | PC合金料 |
| 外形尺寸 | 100 |
| 生产企业 | 美国沙伯基础 |
| 是否进口 | 是 |
不防火高流动PC/ABS CYCOLOY C1204HF
High heat PC/ABS blend offering good flow and excellent IMPACT. Food compliant according to FDA and European directive 2002/72/EC. Available in limited colors. Effective January 15th, 2008 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HC1204HF.
相关色号：HC1204HF-7H1D396、HC1204HF-8H8D215、HC1204HF-8H9D474、HC1204HF- 8H5D150、HC1204HF-8H7D224、HC1204HF-7H1D397、HC1204HF-7H2D323、HC1204HF- 8H5D003、HC1204HF-5H1D001、HC1204HF-2H4D368、HC1204HF-8H4D022、HC1204HF- 8H8D306、HC1204HF-3H6D099、HC1204HF-1H1000、HC1204HF-3H2D038、HC1204HF- 2H1D165、HC1204HF-7H1D529
| TYPICAL PROPERTIES (1) | |||
MECHANICAL机械性能 | Value | Unit | Standard |
Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min | 57 | MPa | ASTM D 638 |
Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min | 47 | MPa | ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min | 5 | % | ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min | 100 | % | ASTM D 638 |
Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min | 2270 | MPa | ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距 | 88 | MPa | ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距 | 2300 | MPa | ASTM D 790 |
Taber Abrasion, CS-17, 1 kg / 泰伯磨耗量, CS-17, 1 kg | 63 | mg/1000cy | SABIC Method |
Tensile Stress, yield 5 mm/min / 抗张程度，屈服, 5 mm/min | 55 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min / 抗张程度,断裂,5mm/min | 45 | MPa | ISO 527 |
Tensile Stress, yield 50 mm/min / 抗张程度，屈服, 50 mm/min | 55 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min | 45 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min / 拉伸伸长,屈服,5mm/min | 5 | % | ISO 527 |
Tensile Strain, break, 5 mm/min / 拉伸伸长,断裂,5mm/min | 100 | % | ISO 527 |
Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min | 4 | % | ISO 527 |
Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min | >50 | % | ISO 527 |
Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min | 2400 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min | 80 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min | 2300 | MPa | ISO 178 |
Hardness, H358/30 / 球压硬度，H358/30 | 96 | MPa | ISO 2039-1 |
Hardness, Rockwell R / 硬度, 洛氏 R | 115 | – | ISO 2039-2 |
IMPACT | Value | Unit | Standard |
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C | 580 | J/m | ASTM D 256 |
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C | 480 | J/m | ASTM D 256 |
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C | 54 | J | ASTM D 3763 |
Izod IMPACT, notched 80*10*3 +23°C / 悬壁梁缺口冲击强度, 80*10*3 +23°C | 50 | kJ/m2 | ISO 180/1A |
Izod IMPACT, notched 80*10*3 -30°C / 悬壁梁缺口冲击强度, 80*10*3 -30°C | 30 | kJ/m2 | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度，23°C，C80*10*3 sp=62mm | 50 | kJ/m2 | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm / 简支梁缺口冲击强度，-30°C，C80*10*3 sp=62mm | 30 | kJ/m2 | ISO 179/1eA |
THERMAL | Value | Unit | Standard |
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50 | 130 | °C | ASTM D 1525 |
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火 | 112 | °C | ASTM D 648 |
CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动 | 7.2E-05 | 1/°C | ASTM E 831 |
CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向 | 7.2E-05 | 1/°C | ASTM E 831 |
Thermal Conductivity / 导热系数 | 0.2 | W/m-°C | ISO 8302 |
CTE, 23°C to 60°C, flow / 线形膨胀系数,23°C 到60°C,流动 | 8.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow / 线形膨胀系数,23°C 到60°C,横向 | 8.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASSES | – | IEC 60695-10-2 |
Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50 | 126 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120 | 128 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm / 热变形温度，0.45 MPa, 未退火, 100 mm 跨距 | 122 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / 热变形温度，1.8 MPa, 未退火, 100 mm 跨距 | 102 | °C | ISO 75/Ae |
Relative Temp Index, Elec / 相对热指数， 电性能 | 60 | °C | UL 746B |
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能 | 60 | °C | UL 746B |
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能 | 60 | °C | UL 746B |
PHYSICAL | Value | Unit | Standard |
Specific Gravity/比重 | 1.15 | – | ASTM D 792 |
Mold Shrinkage on Tensile Bar, flow (2) / 收缩率，流动 | 0.5 – 0.7 | % | SABIC Method |
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm | 0.5 – 0.7 | % | SABIC Method |
Melt Flow Rate / 熔流率, 260°C/5.0 kgf | 24 | g/10 min | ASTM D 1238 |
Density/密度 | 1.15 | g/cm3 | ISO 1183 |
Water Absorption, (23°C/sat) / 吸水率, (23°C/sat) | 0.6 | % | ISO 62 |
Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH) | 0.2 | % | ISO 62 |
Melt Volume Rate, MVR at 260°C/2.16 kg / 溶化体积流率,MVR, 260°C/2.16 kg | 8 | cm3/10 min | ISO 1133 |
Melt Volume Rate, MVR at 260°C/5.0 kg / 溶化体积流率,MVR, 260°C/5.0 kg | 22 | cm3/10 min | ISO 1133 |
ELECTRICAL | Value | Unit | Standard |
Volume Resistivity/体积电阻率 | >1.E+15 | Ohm-cm | IEC 60093 |
Surface Resistivity, ROA / 表面电阻率 | >1.E+15 | Ohm | IEC 60093 |
Dielectric Strength, in oil, 0.8 mm / 耐电强度，在油中，0.8mm | 35 | kV/mm | IEC 60243-1 |
Dielectric Strength, in oil, 1.6 mm / 耐电强度，在油中，1.6mm | 25 | kV/mm | IEC 60243-1 |
Dielectric Strength, in oil, 3.2 mm / 耐电强度，在油中，3.2mm | 17 | kV/mm | IEC 60243-1 |
Relative Permittivity, 50/60 Hz / 相对介电常数，50/60 Hz | 2.8 | – | IEC 60250 |
Relative Permittivity, 1 MHz / 相对介电常数，1 MHz | 2.7 | – | IEC 60250 |
Dissipation Factor, 50/60 Hz / 耗散因素，50/60 Hz | 0.002 | – | IEC 60250 |
Dissipation Factor, 1 MHz / 耗散因素，1 MHz | 0.007 | – | IEC 60250 |
Comparative Tracking Index / 漏电起痕指数 | 250 | V | IEC 60112 |
FLAME CHARACTERISTICS 火焰特性 | Value | Unit | Standard |
UL Recognized, 94HB Flame Class Rating (3) / UL认可，94HB 阻燃等级(3) | 1.2 | mm | UL 94 |
UL Recognized, 94HB Flame Class Rating 2nd value (3) | 3 | mm | UL 94 |
Glow Wire Flammability Index / 灼热丝易燃指数 650°C, passes at | 1 | mm | IEC 60695-2-12 |
Oxygen Index (LOI) / 极限氧指数 | 23 | % | ISO 4589 |
Source GMD, last updated:06/29/2007 |
Processing |
| Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature / 干燥温度 | 100 – 110 | °C |
Drying Time / 干燥时间 | 2 – 4 | hrs |
Maximum Moisture Content / *含湿量 | 0.02 | % |
Melt Temperature / 熔体温度 | 260 – 290 | °C |
Nozzle Temperature / 注嘴温度 | 240 – 280 | °C |
Front – Zone 3 Temperature / 前区3温度 | 250 – 290 | °C |
Middle – Zone 2 Temperature / 中区2温度 | 250 – 290 | °C |
Rear – Zone 1 Temperature / 后区1温度 | 230 – 260 | °C |
Hopper Temperature / 料筒温度 | 60 – 80 | °C |
Mold Temperature / 模具温度 | 60 – 90 | °C |