Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min

51

MPa

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min / 抗拉强度, 断裂, 类型I, 50 mm/min

44

MPa

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min

5

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min

50

%

ASTM D 638

Tensile Modulus, 50 mm/min / 拉伸模量,50 mm/min

2480

MPa

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距

75

MPa

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距

2410

MPa

ASTM D 790

Tensile Stress, yield 50 mm/min / 抗张程度，屈服, 50 mm/min

55

MPa

ISO 527

Tensile Stress, break, 50 mm/min / 抗张程度,断裂,50mm/min

45

MPa

ISO 527

Tensile Strain, yield, 50 mm/min / 拉伸伸长,屈服,,50mm/min

5

%

ISO 527

Tensile Strain, break, 50 mm/min / 拉伸伸长,断裂,50mm/min

15

%

ISO 527

Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min

2400

MPa

ISO 527

Flexural Stress, yield, 2 mm/min / 弯曲强度,屈服,2 mm/min

82

MPa

ISO 178

Flexural Modulus, 2 mm/min / 弯曲模量,2 mm/min

2400

MPa

ISO 178

Hardness, H358/30 / 球压硬度，H358/30

121

MPa

ISO 2039-1

Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C

427

J/m

ASTM D 256

Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C

40

J

ASTM D 3763

Izod IMPACT, notched 80*10*4 +23°C / 悬壁梁缺口冲击强度，80*10*4 +23°C

24

kJ/m2

ISO 180/1A

Izod IMPACT, notched 80*10*4 -30°C / 悬壁梁缺口冲击强度，80*10*4 -30°C

12

kJ/m2

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度，23°C，C80*10*4 sp=62mm

25

kJ/m2

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm / 简支梁缺口冲击强度，-30°C，C80*10*4 sp=62mm

13

kJ/m2

ISO 179/1eA

Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50

143

°C

ASTM D 1525

HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火

131

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火

112

°C

ASTM D 648

CTE, -40°C to 40°C, flow / 线形膨胀系数,-40°C 到40°C,流动

7.2E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow / 线形膨胀系数,-40°C 到40°C,横向

7.2E-05

1/°C

ASTM E 831

Thermal Conductivity / 导热系数

0.2

W/m-°C

ISO 8302

CTE, 23°C to 80°C, flow

8.E-05

1/°C

ISO 11359-2

CTE, 23°C to 80°C, xflow

8.E-05

1/°C

ISO 11359-2

Ball Pressure Test, 125°C +/- 2°C

PASSES

–

IEC 60695-10-2

Vicat Softening Temp, Rate B/50 / 维卡软化温度 B级/50

128

°C

ISO 306

Vicat Softening Temp, Rate B/120 / 维卡软化温度,B级/120

130

°C

ISO 306

HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm / 热变形温度，0.45 MPa, 未退火, 100 mm 跨距

128

°C

ISO 75/Be

HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm / 热变形温度，1.8 MPa, 未退火, 100 mm 跨距

108

°C

ISO 75/Ae

Relative Temp Index, Elec / 相对热指数， 电性能

105

°C

UL 746B

Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能

80

°C

UL 746B

Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能

105

°C

UL 746B

Specific Gravity/比重

1.18

–

ASTM D 792

Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm

0.4 – 0.6

%

SABIC Method

Melt Flow Rate / 熔流率, 260°C/5.0 kgf

22

g/10 min

ASTM D 1238

Density/密度

1.18

g/cm3

ISO 1183

Melt Volume Rate, MVR at 260°C/5.0 kg / 溶化体积流率,MVR, 260°C/5.0 kg

22

cm3/10 min

ISO 1133

Arc Resistance, Tungsten {PLC} / 耐电弧性{PLC}

3

PLC Code

ASTM D 495

Hot Wire Ignition {PLC) / 热丝引燃 {PLC)

3

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC} / 高电流电弧引燃，表面{PLC}

0

PLC Code

UL 746A

Drying Temperature / 干燥温度

105 – 110

°C

Drying Time / 干燥时间

3 – 4

hrs

Drying Time (Cumulative) / 干燥时间（累积的）

8

hrs

Maximum Moisture Content / *含湿量

0.04

%

Melt Temperature / 熔体温度

275 – 300

°C

Nozzle Temperature / 注嘴温度

275 – 300

°C

Front – Zone 3 Temperature / 前区3温度

260 – 300

°C

Middle – Zone 2 Temperature / 中区2温度

255 – 295

°C

Rear – Zone 1 Temperature / 后区1温度

250 – 290

°C

Mold Temperature / 模具温度

60 – 90

°C

Back Pressure / 背压

0.3 – 0.7

MPa

Screw Speed / 螺杆速度

40 – 70

rpm

Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比

30 – 80

%

Vent Depth / 排气孔深度

0.038 – 0.076

mm