Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min

55

MPa

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min

90

%

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距

90

MPa

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距

2250

MPa

ASTM D 790

Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C

678

J/m

ASTM D 256

Izod IMPACT, notched, -40°C / 悬壁梁缺口冲击强度，-40°C

560

J/m

ASTM D 256

HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火

106

°C

ASTM D 648

Specific Gravity/比重

1.13

–

ASTM D 792

Water Absorption, 24 hours / 吸水率， 24小时

0.1

%

ASTM D 570

Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm

0.5 – 0.7

%

SABIC Method

Melt Flow Rate / 熔流率, 260°C/5.0 kgf

8.5

g/10 min

ASTM D 1238

Drying Temperature / 干燥温度

105 – 110

°C

Drying Time / 干燥时间

3 – 4

hrs

Drying Time (Cumulative) / 干燥时间（累积的）

8

hrs

Melt Temperature / 熔体温度

250 – 280

°C