高抗冲击性PC/ABS CYCOLOY C1110HF
在73F 和 -20F时，具有高抗冲击性、高延性。薄壁应用
相关色号：C1110HF-100、C1110HF-BK2E043、C1110HF-YW6D093、C1110HF-701、C1110HF-RD5E062
| TYPICAL PROPERTIES (1) | |||
MECHANICAL机械性能 | Value | Unit | Standard |
Tensile Stress, yld, Type I, 50 mm/min / 抗拉强度,屈服,类型I,50 mm/min | 59 | MPa | ASTM D 638 |
Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸长, 屈服, 类型I, 50 mm/min | 5 | % | ASTM D 638 |
Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸长,断裂,类型I, 50 mm/min | 75 | % | ASTM D 638 |
Tensile Modulus, 50 mm/min / 拉伸模量,50 mm/min | 2200 | MPa | ASTM D 638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span / 挠曲强度, 屈服, 1.3 mm/min, 50 mm 跨距 | 86 | MPa | ASTM D 790 |
Flexural Modulus, 1.3 mm/min, 50 mm span / 挠曲模量, 1.3 mm/min, 50 mm 跨距 | 2370 | MPa | ASTM D 790 |
IMPACT | Value | Unit | Standard |
Izod Impact, notched, 23°C / 悬臂梁缺口冲击强度23°C | 640 | J/m | ASTM D 256 |
Izod IMPACT, notched, -30°C / 悬壁梁缺口冲击强度, -30°C | 267 | J/m | ASTM D 256 |
Instrumented IMPACT Energy @ peak / 仪表控制抗冲击能量 @ 峰值, 23°C | 61 | J | ASTM D 3763 |
Instrumented IMPACT Energy @ peak / 仪表控制抗冲击能量 @ 峰值, -30 | 47 | J | ASTM D 3763 |
Instrumented Impact Total Energy, 23°C / 仪表控制抗冲击总能量，23°C | 61 | J | ASTM D 3763 |
Instrumented IMPACT Total Energy, -30°C / 装有测量仪表的落镖冲击Total Energy，-30°C | 54 | J | ASTM D 3763 |
THERMAL | Value | Unit | Standard |
HDT, 0.45 MPa, 3.2 mm, unannealed / 热变形温度,0.45 MPa, 3.2 mm,未退火 | 126 | °C | ASTM D 648 |
HDT, 1.82 MPa, 3.2mm, unannealed / 热变形温度,1.82 MPa, 3.2mm,未退火 | 110 | °C | ASTM D 648 |
CTE, -30°C to 30°C, flow / 线形膨胀系数,-30°C 到30°C,流动 | 7.2E-05 | 1/°C | ASTM D 696 |
Relative Temp Index, Elec / 相对热指数， 电性能 | 60 | °C | UL 746B |
Relative Temp Index, Mech w/impact / 相对热指数，机械冲击性能 | 60 | °C | UL 746B |
Relative Temp Index, Mech w/o impact / 相对热指数，非机械冲击性能 | 60 | °C | UL 746B |
PHYSICAL | Value | Unit | Standard |
Specific Gravity/比重 | 1.14 | – | ASTM D 792 |
Mold Shrinkage, flow, 3.2 mm / 模塑收缩量，流动，3.2 mm | 0.5 – 0.7 | % | SABIC Method |
Melt Flow Rate / 熔流率, 260°C/3.8 kgf | 12 | g/10 min | ASTM D 1238 |
ELECTRICAL | Value | Unit | Standard |
Arc Resistance, Tungsten {PLC} / 耐电弧性{PLC} | 5 | PLC Code | ASTM D 495 |
Hot Wire Ignition {PLC) / 热丝引燃 {PLC) | 3 | PLC Code | UL 746A |
High Voltage Arc Track Rate {PLC} / 高电压电弧起痕速率 | 1 | PLC Code | UL 746A |
High Ampere Arc Ign, surface {PLC} / 高电流电弧引燃，表面{PLC} | 0 | PLC Code | UL 746A |
Comparative Tracking Index (UL) {PLC} / 漏电起痕指数 (UL) {PLC} | 3 | PLC Code | UL 746A |
FLAME CHARACTERISTICS 火焰特性 | Value | Unit | Standard |
UL Recognized, 94HB Flame Class Rating (3) / UL认可，94HB 阻燃等级(3) | 1.21 | mm | UL 94 |
CSA (See File for complete listing) | LS88480 | File No. | CSA LISTED |
UV-light, water exposure/immersion / 紫外线暴露，耐水/浸渍 | F2 | – | UL 746C |
Source GMD, last updated:01/05/2000 |
Processing |
| Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature / 干燥温度 | 105 – 110 | °C |
Drying Time / 干燥时间 | 3 – 4 | hrs |
Drying Time (Cumulative) / 干燥时间（累积的） | 8 | hrs |
Maximum Moisture Content / *含湿量 | 0.04 | % |
Melt Temperature / 熔体温度 | 275 – 300 | °C |
Nozzle Temperature / 注嘴温度 | 275 – 300 | °C |
Front – Zone 3 Temperature / 前区3温度 | 260 – 300 | °C |
Middle – Zone 2 Temperature / 中区2温度 | 255 – 295 | °C |
Rear – Zone 1 Temperature / 后区1温度 | 250 – 290 | °C |
Mold Temperature / 模具温度 | 60 – 90 | °C |
Back Pressure / 背压 | 0.3 – 0.7 | MPa |
Screw Speed / 螺杆速度 | 40 – 70 | rpm |
Shot to Cylinder Size / 每次注射量占料筒熔胶总量的百分比 | 30 – 80 | % |
Vent Depth / 排气孔深度 | 0.038 – 0.076 | mm |